The Study on the Influence of the Concentration NaCl Solution on Corrosion Fatigue Behavior of T.M.C.P. Steel |
|
|
T.M.C.P. 강의 부식피로거동에 미치는 염분의 영향에 관한 연구 |
이상호,한정섭 |
동아대학교 해양공학과,동아대학교 해양공학과 |
|
© 1993 The Korean Society of Ocean Engineers
Open access / Under a Creative Commons License
|
Keywords:
Corrosion fatigue, T.M.C.P., NaCl |
Abstract |
To study the corrosion fatigue begavior of T.M.C.P. steel, the rotary bending fatigue test with the change of concentration of NaCl solution was carried out. Fatigue life in the corrosion environment is decreased markedly in comparision with that in the air. Fatigue limit in the air was about 225 MPa. In case of 3.5% NaCl solution fatigue life could be expressed as .sigma./sub f/=10,392 * (N/sub f/)/sup -o.2923 . According to the paris's rule, crack growth rates could be expressed as da/dN=2.62.*10/sup -7/ .DELTA. K/sup 1.09/(3.5% NaCl solution), da/dN=1.95 *10/sup -7 .DELTA. K/sup 1.05/(1% NaCl solution), da/dN=2.62 * 10/sup -7/.DELTA./sup 0.72/(0.01% NaCl solution) with da/dN expressed in mm/cycle and .DELTA.K in MPa.GAMMA.m. The crack growth rate in the corrosion environment was highest under 3.5% NaCl solution. |
|